C63000 Nickel Aluminum Bronze is an excellent choice for applications that involve heavy loads, friction and abrasive wear. Adding nickel to the alloy's composition makes the resulting metal stronger without sacrificing its ductility or resistance to corrosion.
Valve Seats, Plunger Tips, Condenser Tube for Power Stations and Desalting Units, Shafting, Pump Parts, Cams, Gears, Valve Guides, Aircraft Parts, Pump Shafts, Structural Members, Corrosion Resistant Articles, Hydraulic Bushings for Earth Moving Equipment, Valve Balls, Bushings, Bearings, Heat Exchanger Flanges, Heat Exchanger Headers, Tanks, Welded Piping Systems, Balls
Nuts, Ship Propellers, Pump Parts, Bolts, Propellers
Faucets
| Cu% | Sn% | Pb% | Zn% | Fe% | Ni% | Sb% | P% | S% | AI% | Mn% | Si% |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Rem. | 0.20 | N/A | 0.30 | 2.00- 4.00 | 4.00- 5.00 | N/A | N/A | N/A | 9.00- 11.00 | 1.50 | 0.25 |
| Mechanical - HR50 Drawn and Stress Relieved Temper: 1/2" to 1" Rod | ||
|---|---|---|
| Tensile Strength, min | 100 ksi | 690 MPa |
| Yield Strength @ .5% ext under load min | 50 ksi | 345 MPa |
| Elongation in 2 in. or 50 mm min, % | 5 | |
| Brinell Hardness | N/A | |
| Machinability Rating | 30% | |
| Mechanical - HR50 Drawn and Stress Relieved Temper: Over 1" to 2" Incl. Rod | ||
|---|---|---|
| Tensile Strength, min | 90 ksi | 620 MPa |
| Yield Strength @ .5% ext under load min | 45 ksi | 310 MPa |
| Elongation in 2 in. or 50 mm min, % | 6 | |
| Brinell Hardness, min | N/A | |
| Machinability Rating | 30% | |
| Mechanical - HR50 Drawn and Stress Relieved Temper: Over 2" to 3" Incl. Rod | ||
|---|---|---|
| Tensile Strength, min | 85 ksi | 585 MPa |
| Yield Strength @ .5% ext under load min | 42.5 ksi | 295 MPa |
| Elongation in 2 in. or 50 mm min, % | 10 | |
| Brinell Hardness, min | N/A | |
| Machinability Rating | 30% | |
| US Customary | Metric | |
|---|---|---|
| Melting Point-Liquidus | 1930 °F | 1054 °C |
| Melting Point-Solidus | 1895 °F | 1035 °C |
| Density | 0.274 lb/in 3 @ 68 °F | 7.58 gm/cm 3 @ 20 °C |
| Specific Gravity | 7.580 | 7.58 |
| Electrical Resistivity | 116 ohms-cmil/ft @ 68 °F | 19.28 microhm-cm @ 20 °C |
| Electrical Conductivity | 7% IACS @ 68 °F | 0.041 MegaSiemens/cm @ 20 °C |
| Thermal Conductivity | 22.6 Btu/sq ft/ft hr/°F @ 68 °F | 39.1 W/m @ 20 °C |
| Coefficient of Thermal Expansion | 9 ⋅ 10-6 per °F (68-572 °F) | 15.5 ⋅ 10-6 per °C (20-300 °C) |
| Specific Heat Capacity | 0.09 Btu/lb/°F @ 68 °F | 377.1 J/kg @ 20 °C |
| Modulus of Elasticity in Tension | 17500 ksi | 120650 MPa |
| Magnetic Permeability | 6400 ksi | 44127 MPa |
| Joining Technique | Suitability |
|---|---|
| Soldering | Not Recommended |
| Brazing | Fair |
| Oxyacetylene Welding | Not Recommended |
| Gas Shielded Arc Welding | Good |
| Coated Metal Arc Welding | Good |
| Spot Weld | Good |
| Butt Weld | Good |
| Capacity for being Cold Worked | Poor |
| Capacity for being Hot Formed | Good |
| Forgeability Rating | 75 |